Abstract This study aimed to evaluate the effect of different concentrations of sodium hypochlorite (NaOCl) and calcium hypochlorite [Ca(OCl)2] on the bond strength and adaptation of glass fiber posts luted with a dual-curing resin cement. Fifty decoronated premolars were sectioned 14 mm from the apex and endodontically treated. The root canal filling was partially removed. The specimens were divided into 5 groups (n=10) according to the irrigant for post space irrigation: 0.9% sodium chloride (NaCl), (control); 2.5% NaOCl; 5.25% NaOCl; 2.5% Ca(OCl)2; and 5.25% Ca(OCl)2. For each group, irrigation was performed with 5 ml of solution. Afterward, the posts were luted with a dual-curing resin cement. One slice from each third was obtained and submitted to the push-out test and failure modes analysis. An additional slice from the middle third was submitted to confocal images for analysis of adaptation failures (gaps). Two-way ANOVA, Tukey’s post-hoc, Kruskal-Wallis with Bonferroni adjusted, and chi-square tests, analyzed data. The group treated with 5.25% NaOCl showed lower bond strength values and generated more cohesive failures compared to the control (p < 0.05). Bond strength decreased from coronal to apical in the post space (p < 0.001). The groups treated with NaOCl had the highest percentages of gaps compared to the control (p < 0.05). Regardless of concentration, Ca(OCl)2 did not influence the bond strength and the occurrence of gaps (P > 0.05). Ca(OCl)2 is a good option for irrigating the post space before luting a fiber post with a dual-curing resin cement.

Resumo Este estudo teve como objetivo avaliar o efeito de diferentes concentrações de hipoclorito de sódio (NaOCl) e hipoclorito de cálcio [Ca(OCl)2] na resistência de união e adaptação de pinos de fibra de vidro cimentados com um cimento resinoso dual. Cinquenta pré-molares tiveram suas coroas removidas, foram seccionados a 14 mm do ápice e tratados endodonticamente. A obturação do canal radicular foi parcialmente removida. Os espécimes foram divididos em 5 grupos (n=10) de acordo com o irrigante para irrigação do espaço do pino: cloreto de sódio 0.9% (NaCl), (controle); NaOCl 2.5%; NaOCl 5.25%; Ca(OCl)2 2.5%; e Ca(OCl)2 5.25%. Para cada grupo, a irrigação foi realizada com 5 ml da solução. Posteriormente, os pinos foram cimentados com um cimento resinoso dual. Uma fatia de cada terço foi obtida e submetida ao teste push-out e análise dos modos de falha. Um corte adicional do terço médio foi submetido a imagens confocais para análise de falhas de adaptação (gaps). Os dados foram analisados pelos testes ANOVA de duas vias, post-hoc de Tukey, Kruskal-Wallis com ajuste de Bonferroni e qui-quadrado. O grupo tratado com NaOCl 5.25% apresentou menores valores de resistência de união e gerou mais falhas coesivas em relação ao controle (p < 0.05). A resistência de união diminuiu de coronal para apical no espaço do pino (p < 0.001). Os grupos tratados com NaOCl apresentaram os maiores percentuais de gaps em relação ao controle (p < 0.05). Independentemente da concentração, o Ca(OCl)2 não influenciou a resistência de união e a ocorrência de gaps (P > 0.05). O Ca(OCl)2 é uma boa opção para irrigar o espaço do pino antes de cimentar um pino de fibra com um cimento resinoso dual.

Aim This review investigated the effect of applying an adhesive after surface treatment of glass-ceramics on the bonding, mechanical or clinical behavior. Methods Studies comparing the adhesive, mechanical or clinical behavior of glass-ceramics, with or without adhesive application after surface treatment, were included. Searches were performed in PubMed, Scopus, and Web of Sciences databases (January 2022), resulting in 15 included studies. Results Regarding the evaluated outcomes, 13 studies assessed bond strength, 2 studies assessed biaxial flexural strength and 1 study assessed fatigue failure load, while no study evaluating clinical outcomes was included. It was possible to observe that the adhesive application after ceramic surface treatment was unfavorable or did not influence the evaluated outcomes. Conclusion Most of the evidence available in the literature shows that the adhesive application after surface treatment does not improve the adhesive and mechanical behavior of glass-ceramics.

Abstract This study aims to evaluate the fatigue resistance of monolithic zirconia (Yz) and multilayer ceramic structures using the CAD-on technique in different thicknesses. Fifty (N=50) standardized single crowns preparations were made in fiberglass-reinforced epoxy resin (NEMA grade G10), digitalized, and restorations were machined in CAD-CAM, composing 5 groups (n= 10): Control: 1.5 mm (milled zirconia framework + manual layered porcelain); Yz monolithic 1.5 mm; Yz monolithic 1.0 mm; CAD-on 1.5 mm; and CAD-on 1.0 mm (milled zirconia framework 0.5 mm thickness bonded by a low fuse ceramic to a milled lithium disilicate layer of 1.0 mm or 0.5 mm, respectively). The G10 bases were conditioned with 10% hydrofluoric acid; the crowns were air abraded with 110 μm alumina particles; and then luted onto each other with self-adhesive resin cement. A cyclic fatigue test was performed (initial load: 400N for 10,000 cycles, frequency of 20 Hz, step size of 200N) until failure, and the data was submitted to a survival statistical analysis. No failures were observed at Yz monolithic 1.5 mm. High and similar performance was observed for Cad-On groups and Yz monolithic 1.0 mm. The control group depicted the worst behavior. The Weibull modulus of CAD-on 1.5 mm was higher than the control while being similar to the other conditions. Both the monolithic systems and the CAD-on technique showed high and similar fatigue fracture behavior and survival rates, which were also higher than the control bilayer system. Both systems reduced the occurrence of delamination failures, making them suitable for clinical use.

Resumo Este estudo teve como objetivo avaliar o comportamento à fadiga de estruturas cerâmicas monolíticas de zircônia (Yz) e multicamadas utilizando a técnica CAD-on em diferentes espessuras. Cinquenta (N=50) preparos unitários padronizados foram confeccionados em resina epóxi reforçada com fibra de vidro (NEMA grau G10), digitalizados e as restaurações usinadas em CAD-CAM, compondo 5 grupos (n= 10): Controle: 1,5 mm (estrutura de zircônia fresada + porcelana estratificada manualmente); Yz monolítica 1,5 mm; Yz monolítica 1,0 mm; CAD-on em 1,5 mm; e CAD-on 1,0 mm (estrutura de zircônia fresada com 0,5 mm de espessura ligada por uma cerâmica de baixa fusão a uma camada de dissilicato de lítio fresado de 1,0 mm ou 0,5 mm, respectivamente). As bases do G10 foram condicionadas com ácido fluorídrico a 10%; as coroas foram jateadas com partículas de alumina de 110 μm; e então cimentadas uma sobre a outra com cimento resinoso autoadesivo. Foi realizado um teste de fadiga cíclica (carga inicial: 400N para 10.000 ciclos, frequência de 20 Hz, step de 200N) até a falha, e os dados foram submetidos a uma análise estatística de sobrevivência. Nenhuma falha foi observada para Yz monolítica de 1,5 mm. Desempenho alto e semelhante foi observado para os grupos Cad-On e Yz monolítica 1,0 mm. O grupo controle apresentou o pior comportamento. O módulo de Weibull do CAD-on 1,5 mm foi maior que o grupo controle, sendo semelhante às outras condições. Tanto os sistemas monolíticos quanto a técnica CAD-on apresentaram alto e semelhante desempenho mecânico e taxas de sobrevivência, que também foram superiores ao sistema bicamada de controle. Ambos os sistemas reduziram a ocorrência de falhas de delaminação, tornando-os adequados para uso clínico.